http://dspace.mediu.edu.my:8181/xmlui/handle/10261/4136| Title: | Las escorias de la central térmica GICC ELCOGAS como materia prima para la síntesis de materiales vitrocerámicos. Parte 2: Síntesis y caracterización de los materiales vitrocerámicos The slag from ELCOGAS IGCC thermal power plant as raw material for the synthesis of glass-ceramic materials. Part 2: Synthesis and characterization of the glass-ceramic materials |
| Keywords: | Residuos de gasificación de carbón Escorias GICC Desvitrificación Vitrocerámicos de wolastonita / anortita Materiales porosos Coal gasification wastes IGCC slag Devitrification Anorthite / wollastonite glassceramics Porous materials |
| Publisher: | Sociedad Española de Cerámica y Vidrio |
| Description: | [ES] Se expone en este trabajo la segunda parte de los resultados de la investigación sobre el comportamiento en fusión de las
escorias y el proceso seguido para la obtención de materiales vitrocerámicos utilizando estas escorias como materia prima.
A partir de una mezcla vitrificable basada en escorias, casco de vidrio y carbonato cálcico precipitado de azucarera, se ha
obtenido por fusión a 1450ºC un vidrio (ECSCP) que presenta un mecanismo de cristalización superficial.
Con el vidrio pulverizado se conformaron probetas cilíndricas de 40 mm de diámetro y 7 mm de altura aproximada, que
fueron posteriormente sometidas a los tratamientos térmicos de desvitrificación a temperaturas entre 800 y 1100ºC, y
tiempos de tratamiento entre 5 y 60 minutos, obteniéndose una serie de materiales vitrocerámicos de wollastonita-anortitagehlenita.
Estos materiales han sido caracterizados y analizadas sus propiedades en función del tiempo y las temperaturas
de desvitrificación. [EN] There are here reported the result of the second phase of the investigation on the melting behavior of the slag and the process followed to synthesize glass-ceramic materials using this slag as raw component. Starting from a vitrifying mixture based on slag, glass cullet and precipitated calcium carbonate coming from sugar refining, we have obtained the parent glass named ECSCP, which exhibit a surface tendency of crystallization. Pressed specimens of 40 mm diameter and 7 mm height were conformed with the powdered ECSCP glass. The specimens were heat treated for crystalline phases development at temperatures between 800 and 1100ºC during time intervals from 5 to 60 minutes. A series of wollastonite-anorthite-gehlenite glass-ceramics has been synthesized of different characteristics depending on the time and temperature of devitrification. Las siguientes entidades han colaborado en la financiación de esta investigación: la Comisión Interministerial de Ciencia y Tecnología a través del proyecto REN2001-0912/TECNO; las empresas ELCOGAS S.A y Azucarera EBRO S.L. Peer reviewed |
| URI: | http://dspace.mediu.edu.my:8181/xmlui/handle/10261/4136 |
| Other Identifiers: | Boletín de la Sociedad Española de Cerámica y Vidrio 45(1): 28-32 (2006) 0366-3175 http://hdl.handle.net/10261/4136 |
| Appears in Collections: | Digital Csic |
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.