http://dspace.mediu.edu.my:8181/xmlui/handle/10261/4720| Title: | Obtención de materiales de magnesia – circonato cálcico – silicato dicálcico por sinterización reactiva de mezclas de dolomita – circón. Estudio del procesamiento Synthesis of magnesia - calcium zirconate – dicalcium silicate materials by reaction sintering of dolomite – zircon mixtures. Processing study |
| Authors: | Comisión Interministerial de Ciencia y Tecnología, CICYT (España) Consejo Superior de Investigaciones Científicas (España) Consejo Nacional de Ciencia y Tecnología (México) |
| Keywords: | Procesamiento Sinterización reactiva Dolomita Magnesia Circonato cálcico Microestructura Processing Reaction sintering Dolomite Calcium Zirconate Microestructure |
| Publisher: | Sociedad Española de Cerámica y Vidrio |
| Description: | [ES] Se ha estudiado la interdependencia entre la densidad en verde y el tamaño de partícula en la sinterización reactiva de mezclas
de circón – dolomita. El tamaño del polvo se ha determinado con un analizador de partícula por láser y se ha controlado
variando el tiempo de molienda en un molino de atrición. Se ha observado que para un mismo método de consolidación
la densidad de los compactos, en verde, esta relacionada con la distribución de tamaño de partícula. La densidad en verde y
el grado de aglomeración influyen sobre la sinterización de la mezcla de polvos. Los datos experimentales indican que compactos
con similar densidad en verde y menor número de aglomerados presentan un mejor comportamiento durante la sinterización.
Se ha probado que los parámetros significativos en el proceso son el tamaño de partícula y/o aglomerado y características
de la mezcla tales como homogeneidad y grado de compactación. [EN] The interdependence of green density and particle size and their influence on the reaction sintering behaviour of zircon - dolomite powder mixtures were investigated. Powder size was controlled by attrition-milling for different times and was defined as the average size obtained by laser particle size analysis. Green compact density was shown to be related to the powder particle size distribution for identical consolidation conditions. Both the green density and the degree of powder agglomeration affect the sinter behaviour over the entire process. The experimental results showed that compacts with similar green density and which contained fewer coarse particles had a better sintering behaviour. The most important controlling parameters are characteristics of the raw materials as particle or agglomerate particle size and particle size distribution, homogeneity and compaction of the raw materials and sintering temperature. Los autores agradecen la ayuda económica recibida de la CICYT, España, a través del proyecto MAT 2000-0941, y del proyecto cooperativo CSIC/CONACYT 99MX0023. Uno de los autores agradece la concesión de una beca al CONACYT México. Peer reviewed |
| URI: | http://dspace.mediu.edu.my:8181/xmlui/handle/10261/4720 |
| Other Identifiers: | Boletín de la Sociedad Española de Cerámica y Vidrio 40(6): 461-469 (2001) 0366-3175 http://hdl.handle.net/10261/4720 |