http://dspace.mediu.edu.my:8181/xmlui/handle/1957/5757| Title: | Fatigue and fracture of bulk metallic glasses : role of free volume |
| Authors: | Kruzic, Jamie J Busch, Ralf Li, Chunfei Cann, David Higgins, Christopher Pavol, Mickael |
| Keywords: | Fatigue Fracture Bulk Metallic Glasses Free Volume Structural Relaxation |
| Issue Date: | 16-Oct-2013 |
| Description: | Graduation date: 2008 Deformation of metallic glasses requires the existence of free volume to allow atomic movement under mechanical loading. Accordingly, the present research seeks to understand how free volume variations in alloys of identical compositions affect the fatigue and fracture behavior. By annealing below the glass transition temperature, the free volume of a Zr-based bulk metallic glass was varied via structural relaxation. Differential scanning calorimetry was used to quantify enthalpy differences between the relaxed and as-cast materials which are then related to free volume differences. Although structural relaxation showed a pronounced effect in reducing the fracture toughness, a reduction in free volume increases the fatigue strength of the bulk amorphous alloy. Mechanistically, the fatigue properties associated with a free volume variation differ significantly with respect to crack initiation. Surprisingly, the fatigue crack-growth behavior was found to be relatively insensitive to bulk free volume differences. Depth-profiled Doppler broadening spectroscopy (DBS) was utilized to perform local depth profiling of fatigue fracture surfaces to characterize local free volume differences. It’s demonstrated that the intense deformation near a fatigue crack tip result in a local increase in free volume, which in turn determines the local flow properties. The effect of residual stresses on the fatigue and fracture behavior was also investigated. The superimposition of compressive stresses induced by thermal tempering during processing was found to retard fatigue crack propagation and to improve the fracture toughness. |
| URI: | http://koha.mediu.edu.my:8181/xmlui/handle/1957/5757 |
| Other Identifiers: | http://hdl.handle.net/1957/5757 |
| Appears in Collections: | ScholarsArchive@OSU |
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.